Desktop Factory Inc. is the probable assignee for a patent application from Bedal and Schmidt. Aluminum filler is said to increase the speed of sintering the thermoplastic base material by increasing thermal conductivity. Additives may include light absorbers, flow agents and other materials. The material is claimed to offer low curl and good mechanical properties.
Z Corporation has applied for a patent on a material system that uses a peroxide cure with an acrylate binder to form parts having high strength without subsequent infiltration.

From Update 52 - 9/4/07 to 12/4/07:

Toyota Motorsport GmbH and EOS GmbH (both of Germany) are co-assignees for a patent application concerning laser sintering materials with improved properties. Spherical plastic powders incorporate reinforcing fibers while retaining good flow characteristics.
Timothy Moore et al (Australia) describe biodegradable polyurethane and polyurethane ureas suitable for use in fused deposition modeling (FDM) in their patent application. The materials can be used for tissue engineering and repair.

From Update 51 - 6/6/07 to 9/4/07:

Degussa AG (Germany) has described a process which can convert a wide range of irregularly-shaped powder particles to a spherical shape which is preferable in SLS/SLM applications. Materials are mechanically kneaded with various sugar-based materials which are subsequently leached away. See Fig. 7.

From Update 49 - 12/5/06 to 3/6/07:

A process for coating plastic or other non-conductive parts with a metal layer is described in a patent application this quarter. It's said to improve corrosion resistance, wear and strength, and may offer a competitive alternative to the commercially-available RepliForm process.
DSM BV (Netherlands) is the assignee for a patent application material for making colored SLA parts. It offers attractive appearance and the added advantages of being able to monitor building progress and accuracy in removing uncured resin.

From Update 48 - 9/5/06 to 12/5/06:

A new material approach describes a way to get around inaccuracy problems caused by binder shrinkage in three dimensional printing. Very small glass particles are adhered to the surface of the main build material particles. As the binder cures, the glass particles act as tiny spacers to maintain the position of the build material particles in the matrix. See Fig. 2.